Coupling well structure for improving HVMOS performance

ABSTRACT

A semiconductor structure includes a substrate, a first well region of a first conductivity type overlying the substrate, a second well region of a second conductivity type opposite the first conductivity type overlying the substrate, a cushion region between and adjoining the first and the second well regions, an insulation region in a portion of the first well region and extending from a top surface of the first well region into the first well region, a gate dielectric extending from over the first well region to over the second well region, wherein the gate dielectric has a portion over the insulation region, and a gate electrode on the gate dielectric.

This application is a continuation of U.S. patent application Ser. No.12/362,307, filed Jan. 29, 2009, and entitled “Coupling Well Structurefor Improving HVMOS Performance,” which further claims the benefit ofU.S. patent application Ser. No. 11/594,508, filed Nov. 8, 2006, andentitled “Coupling Well Structure for Improving HVMOS Performance,”which claims the benefit of U.S. Provisional Application No. 60/852,183,filed on Oct. 17, 2006, entitled “Coupling Well Structure for ImprovingHVMOS Performance,” which applications are hereby incorporated herein byreference.

TECHNICAL FIELD

This invention relates generally to semiconductor devices, and moreparticularly to metal-oxide-semiconductor (MOS) devices, and even moreparticularly to the structure and manufacturing methods of high-voltageMOS devices.

BACKGROUND

High-voltage metal-oxide-semiconductor (HVMOS) devices are widely usedin many electrical devices, such as input/output (I/O) circuits, CPUpower supplies, power management systems, AC/DC converters, etc. HVMOSdevices typically include drain regions and laterally-diffused drainregions enclosing drain regions. Laterally-diffused drain regions aretypically well regions having lower doping concentrations than the drainregions, thus having high breakdown electrical fields.

FIG. 1 illustrates a conventional HVNMOS device 2, which includes gateoxide 10, gate electrode 12 on gate oxide 10, drain region 6 in n-wellregion 4, and source region 8 in p-well region 7. Shallow trenchisolation (STI) region 14 spaces drain region 6 apart from gateelectrode 12 so that a high drain-to-gate voltage can be applied.

It is known that high electrical fields are typically generated atinterface regions. For HVNMOS device 2, when a high voltage is appliedbetween drain region 6 and source region 8, a high electrical field isgenerated at a region proximate p-n junction 16, which becomes the weakpoint of the HVNMOS device 2. The generation of the high electricalfield causes the reduction in breakdown voltage of HVNMOS device 2. Thisproblem worsens when the device dimensions become smaller, and thus theelectrical fields become higher.

Novel methods for reducing electrical fields at p-n junctions are thusneeded to improve breakdown voltages of high-voltage MOS devices.

SUMMARY OF THE INVENTION

In accordance with one aspect of the present invention, a semiconductorstructure includes a substrate, a first well region of a firstconductivity type overlying the substrate, a second well region of asecond conductivity type opposite the first conductivity type overlyingthe substrate, a cushion region between and adjoining the first and thesecond well regions, an insulation region in a portion of the first wellregion and extending from a top surface of the first well region intothe first well region, a gate dielectric extending from over the firstwell region to over the second well region, wherein the gate dielectrichas a portion over the insulation region, and a gate electrode on thegate dielectric.

In accordance with another aspect of the present invention, asemiconductor structure includes a substrate, a first well region of afirst conductivity type overlying the substrate, a second well region ofa second conductivity type opposite the first conductivity typeoverlying the substrate, wherein the first and the second well regionshave an overlap region, an insulation region extending from a topsurface of the first well region into the first well region, a gatedielectric extending from over the first well region to over the secondwell region, wherein the gate dielectric has an edge directly over theinsulation region, and a gate electrode on the gate dielectric.

In accordance with yet another aspect of the present invention, asemiconductor structure includes a substrate, a first well region havinga first impurity of a first conductivity type overlying the substrate, asecond well region having a second impurity of a second conductivitytype opposite the first conductivity type overlying the substrate,wherein the first and the second well regions have a space therebetween,an insulation region in a portion of the first well region and extendingfrom a top surface of the first well region into the first well region,a gate dielectric extending from over the first well region to over thesecond well region, wherein the gate dielectric has an edge directlyover the insulation region, and a gate electrode on the gate dielectric.

In accordance with yet another aspect of the present invention, a methodof forming a semiconductor structure includes providing a substrate,forming a first well region of a first conductivity type overlying thesubstrate, forming a second well region of a second conductivity typeopposite the first conductivity type overlying the substrate, wherein acushion region is formed adjoining the first and the second wellregions, forming an insulation region in a portion of the first wellregion and extending from a top surface of the first well region intothe first well region, forming a gate dielectric extending from over thefirst well region to over the second well region, wherein the gatedielectric has a portion over the insulation region, and forming a gateelectrode on the gate dielectric.

In accordance with yet another aspect of the present invention, a methodof forming a semiconductor structure includes proving a substrate,forming a first well region of a first conductivity type overlying thesubstrate, forming a second well region of a second conductivity typeopposite the first conductivity type overlying the substrate, whereinthe first and the second well regions have an overlap region, forming aninsulation region in a portion of the first well region and extendingfrom a top surface of the first well region into the first well region,forming a gate dielectric extending from over the first well region toover the second well region, wherein the gate dielectric has an edgedirectly over the insulation region, and forming a gate electrode on thegate dielectric.

The cushion region between the p-well region and the n-well regionincreases the breakdown electrical field at the interface region of thep-well region and the n-well region. The breakdown voltage of therespective high-voltage device is thus increased.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the present invention, and theadvantages thereof, reference is now made to the following descriptionstaken in conjunction with the accompanying drawings, in which:

FIG. 1 illustrates a conventional HVNMOS device;

FIGS. 2 through 7 are cross-sectional views of intermediate stages inthe manufacture of a first embodiment of the present invention, whereina cushion region is formed by overlapping a p-well region and an n-wellregion;

FIGS. 8 and 9 illustrate a second embodiment of the present invention,wherein a cushion region formed by spacing a p-well region apart from ann-well region;

FIG. 10 illustrates a symmetric embodiment of the present invention; and

FIG. 11 illustrates a comparison between substrate currents of aconventional high-voltage MOS device and an embodiment of the presentinvention.

DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS

The making and using of the presently preferred embodiments arediscussed in detail below. It should be appreciated, however, that thepresent invention provides many applicable inventive concepts that canbe embodied in a wide variety of specific contexts. The specificembodiments discussed are merely illustrative of specific ways to makeand use the invention, and do not limit the scope of the invention.

The preferred embodiments of the present invention are described withreference to FIGS. 1 through 7. Variations of the preferred embodimentsare then discussed. Throughout the various views and illustrativeembodiments of the present invention, like reference numbers are used todesignate like elements.

Referring to FIG. 2, substrate 20 is provided. Substrate 20 preferablyincludes a semiconductor material such as silicon, SiGe, or a compoundof group III and group IV elements. Substrate 20 may be a bulk materialor have a silicon-on-insulator (SOI) structure. Preferably, substrate 20is lightly doped with a p-type impurity, although it can also be dopedwith an n-type impurity.

FIG. 2 also illustrates the formation of n-well region 24. Photoresist22 is first applied and patterned. In the preferred embodiment, n-wellregion 24 is implanted with n-type impurities, such as phosphorousand/or arsenic. Preferably, n-well region 24 is a high-voltage n-wellregion, which has a low impurity concentration. In alternativeembodiments, n-well region 24 is a low-voltage n-well (LVNW) region thatis formed simultaneously with the formation of the n-well regions oflow-voltage PMOS devices (not shown). In an exemplary embodiment, then-type impurity concentration in n-well region 24 is between about10¹⁴/cm³ to about 10¹⁷/cm³. After the formation of n-well region 24,photoresist 22 is removed.

Referring to FIG. 3A, photoresist 26 is applied, and p-well regions 28and 30 are formed, which are implanted with p-type impurities, such asboron and/or indium. Preferably, p-well regions 28 and 30 arehigh-voltage n-well regions with a low impurity concentration. Inalternative embodiments, p-well regions 28 and 30 are low-voltage p-well(LVPW) regions that are formed simultaneously with the formation of thep-well regions of low-voltage NMOS devices (not shown). In an exemplaryembodiment, the p-type impurity concentration in p-well regions 28 and30 is between about 10¹⁴/cm³ to about 10¹⁷/cm³. After the formation ofp-well regions 28 and 30, photoresist 26 is removed.

In the embodiments discussed in preceding paragraphs, p-well regions 28and 30 and n-well region 24 are formed by implanting substrate 20. Inalternative embodiments, the well regions are formed by epitaxialgrowth. In an exemplary embodiment, as shown in FIG. 3B, an N+ buriedlayer (NBL) 23 is formed in a top region of the substrate 20. NBL 23 ispreferably formed by implanting or in-situ doping impurities into thetop surface of substrate 20. For example, antimony and/or arsenic may beimplanted or in-situ doped to an impurity concentration of about10¹⁶/cm³ to about 10¹⁸/cm³.

An epitaxial layer 25 is then epitaxially grown on NBL 23. Epitaxiallayer 25 preferably comprises a semiconductor such as silicon, and morepreferably the same material as substrate 20, and is preferably dopedwith one of the p-type and n-type impurities. Assuming p-type impuritiesare doped, the impurity concentration is then equal to the desiredconcentration of p-well regions 28 and 30. A photoresist (not shown) isthen formed and patterned, exposing region 24. An n-type impurityimplantation is then performed. The implanted n-type impurityneutralizes the p-type impurities in epitaxial layer 25 and converts theimplanted region to n-well region 24. Un-implanted epitaxial regionsthus form p-well regions 28 and 30. Alternatively, the epitaxial layer25 may be doped with n-type impurities when grown, and implanted withp-type impurities.

In both FIGS. 3A and 3B, p-well region 28 and n-well region 24 have anoverlap region 32, which is referred to as cushion region 32hereinafter. Preferably, width C of cushion region 32 is between about10 Å and about 3 μm, and more preferably between about 0.3 μm and about0.5 μm.

FIG. 4 illustrates the formation of insulation regions 44. In thepreferred embodiment, insulation regions 44 are formed by formingshallow trenches, filling the trenches with a dielectric material, suchas high-density plasma (HDP) oxide, and performing a chemical mechanicalpolish to remove excess dielectric material. The resulting shallowtrench isolation (STI) regions are insulation regions 44. In otherembodiments, a mask layer (not shown), for example, a SiN layer, isformed over the previously formed structure. The mask layer is thenpatterned to form openings. An oxidation is then performed, andinsulation regions (also referred to as field oxides) 44 are formed inthe openings.

Referring to FIG. 5, photoresist 48 is applied and patterned. A p-typeimpurity implantation is performed, forming P+ region 52. Preferably, P+region 52 comprises boron and/or other p-type impurities, and is heavilydoped to a concentration of greater than about 10²⁰/cm³. P+ region 52may act as the pick-up region of the p-well region 28. After theimplantation, photoresist 48 is removed.

Referring to FIG. 6, photoresist 54 is applied and patterned, and ann-type impurity implantation is performed, forming N+ regions 56 and 58.The implanted impurities may comprise phosphorus and/or arsenic.Preferably, the n-type impurities are heavily doped to a concentrationof greater than about 10²⁰/cm³. N+ regions 56 and 58 act as a draincontact region and source region, respectively. Photoresist 54 is thenremoved.

Alternatively, N+ regions 56 and 58 may be formed before the formationof P+ region 52, or formed after the formation of gate dielectric, gateelectrode and gate spacers. One skilled in the art will realize therespective process steps.

FIG. 7 illustrates the formation of gate dielectric 60, gate electrode62 and gate spacers 64. As is known in the art, gate dielectric 60preferably comprises silicon oxide, although other dielectric materialssuch as silicon nitride, silicon carbide, silicon oxynitride,combinations thereof, and multi-layers thereof, can be used. Gateelectrode 62 preferably includes doped polysilicon. Alternatively,metals, metal nitrides, metal silicides, and other conductive materialscan be used. Gate spacers 64 are preferably formed by blanket forming adielectric material, and removing undesired portions from horizontalsurfaces. The details for forming gate dielectric 60, gate electrode 62and gate spacers 64 are well known in the art, and thus are not repeatedherein. Preferably, an edge of gate electrode 62 is located directlyover insulation region 44 in n-well region 24. HVNMOS device 66 is thusformed.

A second embodiment of the present invention is illustrated in FIGS. 8and 9. This embodiment is similar to the embodiment shown in FIG. 7,except that cushion region 32 is a space between p-well region 28 andn-well region 24. In an exemplary embodiment, a structure as shown inFIG. 2 is formed. Photoresist 26, as shown in FIG. 8 is then formed forthe formation of p-well regions 28 and 30. P-well region 28 and n-wellregion 24 are thus spaced apart, forming cushion region 32. It is to berealized that impurities in n-well region 24 and p-well region 28 arelikely to diffuse into cushion region 32. However, the diffused impurityconcentration will be low compared to the impurity concentrations inrespective n-well region 24 and p-well region 28. In an exemplaryembodiment, the p-type and n-type impurities diffuse into cushion region32 and form a p-n junction therein. The ratios of p-type and n-typeimpurities concentration at the p-n junction to the p-type and n-typeimpurities in respective n-well region 24 and p-well region 28 arelikely to be less than ⅕, even less than 0.1. With an adequate width Wof cushion region 32, the ratios may even be less than about 0.01.Similar to the first embodiment, width C of cushion region 32 ispreferably between about 10 Å and about 3 μm, and more preferablybetween about 0.3 μm and about 0.5 μm.

The previously illustrated embodiments have asymmetric structures,wherein source and drain regions are in well regions with differentconductivity types. FIG. 10 illustrates a HVNMOS embodiment having asymmetric structure, wherein the HVNMOS device includes two n-wellregions 70, 72 and a p-well region 74 therebetween. Similar to theembodiment illustrated in FIG. 7, cushion regions 76 and 78 are formed,wherein each of the cushion regions 76 and 78 may be an overlap regionor a spacing between the neighboring p-well and n-well regions. Inalternative embodiments, p-well region 74 only overlaps (or spaced apartfrom) one of the n-well regions 70 and 72, so that only one of thecushion regions 76 and 78 are formed, while a conventional interface isformed between p-well region 74 and the other adjacent n-well region.

Although the preferred embodiments illustrate the formation of HVNMOSdevices, one skilled in the art will realize the respective formationsteps for forming HVPMOS devices, with the conductivity type of n-wellregion 24, p-well regions 28 and 30, and N+ regions 56 and 58, etc.,reversed (refer to FIGS. 7 and 9). It should also be appreciated thatHVMOS devices have various different layouts. However, the concept ofthe present invention may still be applied. Similarly, a symmetricHVPMOS device may be formed by reversing the conductivity types of thedoped regions in FIG. 10.

Besides forming HVMOS devices, the concept of forming a cushion regionto affect the distribution of electrical fields may be applied to theformation of other devices, such as diodes. By forming cushion regionsbetween p-type and n-type regions of p-n junctions, the breakdownvoltage of diodes can be improved.

An advantageous feature of the present invention is that n-well region24 and p-well region 28 are separated from each other by cushion region32. Inside cushion region 32, the net impurity concentration is low. Inthe embodiment shown in FIG. 7, in cushion region 32, the p-typeimpurities and n-type impurities neutralize each other, and thus the netimpurity concentration is reduced. In the embodiment shown in FIG. 9,cushion region 32 is not doped during the formation of well regions, andthus the impurity concentration is low. Therefore, the cushion region 32form an interface region with lower net impurity concentrations, andthus the performance of the HVMOS devices is improved. Experiments haverevealed that the breakdown voltages of the embodiment of the presentinvention are improved about 3 volts to about 5 volts over the breakdownvoltages of conventional HVMOS devices with similar structures (exceptno cushion regions are formed). In addition, as is shown in FIG. 11,substrate currents Isub of embodiments of the present invention aresignificantly lower than substrate currents of conventional HVMOSdevices. The Isub of an embodiment of the present invention isillustrated as line 80, which has a maximum Isub of about only 2E-06A/μm, while Isub of a conventional HVMOS device is illustrated as line82, which has a maximum Isub of about 6.5E-06 A/μm. As is known in theart, the lifetime of HVMOS devices is strongly related to Isub. WithIsub reduced, the lifetime of HVMOS devices will be increased.

Although the present invention and its advantages have been described indetail, it should be understood that various changes, substitutions andalterations can be made herein without departing from the spirit andscope of the invention as defined by the appended claims. Moreover, thescope of the present application is not intended to be limited to theparticular embodiments of the process, machine, manufacture, andcomposition of matter, means, methods and steps described in thespecification. As one of ordinary skill in the art will readilyappreciate from the disclosure of the present invention, processes,machines, manufacture, compositions of matter, means, methods, or steps,presently existing or later to be developed, that perform substantiallythe same function or achieve substantially the same result as thecorresponding embodiments described herein may be utilized according tothe present invention. Accordingly, the appended claims are intended toinclude within their scope such processes, machines, manufacture,compositions of matter, means, methods, or steps.

1. A semiconductor structure comprising: a substrate; a first wellregion of a first conductivity type overlying the substrate; a secondwell region of a second conductivity type opposite the firstconductivity type overlying the substrate; a first cushion regionbetween the first and the second well regions, wherein the cushionregion is an overlap region of the first and the second well regions; athird well region of the first conductivity type overlying thesubstrate; a second cushion region between the second and the third wellregions, wherein the second cushion region is an overlap region of thesecond and the third well regions; an insulation region extending from atop surface of the first well region into the first well region, whereinthe first and the second cushion regions are horizontally spaced apartfrom the insulation region; a gate dielectric extending from directlyover the first well region to directly over the second and the thirdwell regions; a gate electrode on the gate dielectric; a gate spacer ona sidewall of the gate electrode; a drain region in the first wellregion and adjoining the insulation region; and a source region in thethird well region and underlying an edge of the gate spacer.
 2. Thesemiconductor structure of claim 1, wherein an entirety of the firstcushion region and an entirety of the second cushion region are directlyunderlying the gate dielectric.
 3. The semiconductor structure of claim1, wherein a portion of the second well region not overlapping any ofthe first and the third well regions spaces the first and the secondcushion regions apart from each other.
 4. The semiconductor structure ofclaim 3, wherein the width of at least one of the first cushion regionand the second cushion region is between about 0.3 μm and about 3 μm. 5.The semiconductor structure of claim 1, wherein one of the first and thesecond cushion regions has a width between about 10 Å and about 3 μm. 6.The semiconductor structure of claim 1, wherein the first and the thirdwell regions have impurity concentrations between about 10¹⁴/cm³ andabout 10¹⁷/cm³, and wherein the second well region has an impurityconcentration between about 10¹⁴/cm³ and about 10¹⁷/cm³.
 7. Asemiconductor structure comprising: a p-type substrate; a first n-wellregion overlying the p-type substrate; a p-well region overlying thep-type substrate; a first cushion region between the first n-well regionand the p-well region, wherein the first cushion region is an overlapregion of the first n-well region and the p-well region, and wherein thefirst cushion region has a width greater than about 0.3 μm; a secondn-well region overlying the p-type substrate; a second cushion regionbetween the second n-well region and the p-well region, wherein thesecond cushion region is an overlap region of the second n-well regionand the p-well region, wherein the second cushion region has a widthgreater than about 0.3 μm, and wherein a portion of the p-well regionnot overlapping any of the first and the second n-well regions spacesthe first and the second cushion regions apart from each other; aninsulation region extending from a top surface of the first n-wellregion into the first n-well region; a gate dielectric directly overportions of the first and the second n-well regions and the p-wellregion, and directly over a portion of the insulation region; a gateelectrode over the gate dielectric; a sidewall spacer on a sidewall ofthe gate electrode; a drain region in the first n-well region andadjoining the insulation region; and a source region in the secondn-well region and underlying the sidewall spacer.
 8. The semiconductorstructure of claim 7, wherein the first and the second cushion regionsare horizontally spaced apart from the insulation region.
 9. Thesemiconductor structure of claim 7, wherein one of the first and thesecond cushion regions has a width between about 0.3 μm and about 3 μm.10. The semiconductor structure of claim 7, wherein the first and thesecond n-well regions have impurity concentrations between about10¹⁴/cm³ and about 10¹⁷/cm³.
 11. The semiconductor structure of claim 7,wherein the p-well region has an impurity concentration between about10¹⁴/cm³ and about 10¹⁷/cm³.